| Customization: | Available |
|---|---|
| CAS No.: | 27837-75-8 |
| Formula: | (C8h4o3.C4H2O3.C2h6o2)X |
|
Still deciding? Get samples of $ !
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
TM-51003 is a high performance anchoring resin with fast curing time (adjustable speed), fast strength growth and high strength. It can withstand loads in time after construction, and has high anchoring force and good fatigue strength. It is widely used in pre-stressed anchor reinforcement such as roadway support, wellbore installation, and hydropower engineering. It is also widely used in building reinforcement, tunnel construction, equipment foundation and component anchoring.
2,Liquid resin technical data:
| Item | unit | index | Test standard |
| appearance | -- | Yellow transparent liquid | GB/T 8237.4.1.1 |
| viscosity | 25ºC,Pa.S | 0.16~0.32 | GB/T 7193.1 |
| Gel time | 25ºC,s | 80~140 | GB/T 7193.6 |
| acid value | mgKOH/g | 18~26 | GB/T 2895 |
| non-volatile | % | 57~63 | GB/T 7193.3 |
| Item | unit | Index | Test standard |
| Barcol Hardness | 45 | GB3854-83 | |
| HDT | ºC | 92 | GB/T1634-04 |
| Bending strength | MPa | 121 | GB/T2570-95 |
Remark:casting matrix should follow GB8237-2005
Hardness system: hardener Butanox M-50 1.5% ,Accelerator 0.8% Co/oct 1.0%
Later Hardness system:room temperature ×24 hours + 60ºCX3hours+120ºC×2 hours
Other Unsaturated Polyester Resin:
| 1: Hand lay-up General purpose | ||||||||||
| Code | Type | 25º C PA. S | Min | % | MPa | % | MPa | HDT | Application | |
| Viscosity | Gel time | Non-Volatile | Tensile | Elongation | Flexural | |||||
| Strength | Strength | |||||||||
| TM-189 | PA | 0.25-0.45 | 10-22 | 59-65 | 60 | 4 | 100 | 57 | Water resistance, for boat. CCS | |
| TM-191 | PA | 0.25-0.45 | 9-17 | 61-67 | 55 | 1.8 | 110 | 66 | Translucent, general FRP purpose | |
| TM-191RS | PA | 0.25-0.45 | 9-17 | 61-67 | 60 | 3.5 | 114 | 70 | For FRP product, general purpose | |
| TM-196 | PA | 0.60-1.20 | 9.1-18.9 | 64-70 | 76 | 2 | 120 | 72 | Flexibility, high strength, CCS | |
| TM-580 | IPA | 0.40-0.70 | 10-20 | 66-70 | 15 | 68 | 10 | 67 | Flexibilizer or flexible resin, with other resins | |
| TM-1032 | PA | 0.25-0.65 | 15-23 | 15-23 | 60 | 2 | 105 | 67 | Good mechanical property, for bus, boat, CCS approval | |
| TM-22 | PA | 0.34-0.38 | 16-22 | 16-22 | 62 | 2.3 | 108 | 65 | Pre-promoted, thixotropy and low shrinkage | |
| TM-2068 | PA | 0.20-0.40 | 11-25 | 11-25 | 58 | 1.5 | 110 | 100 | Hot water resistance and high HDT, for bathtub | |
| TM-10070 | PA | 0.30-0.34 | 8-18 | 8-18 | 65 | 2 | 115 | 68 | Low viscosity, rapid wetting reinforcement for high strength FRP products. | |