Fiberglass Biaxile Fabrics 450g, in +45/-45 Degree

• Customization: Available
• Certification: ISO
• Technique: Needle Mat
• Model NO.: Biaxial Fabric (+45/-45 degree)
• Mat Type: Combination Mat
• Fiberglass Type: E-Glass
• Width: 1270mm
• Roll Weight: 50kg
• Transport Package: Carton
• Specification: WIDTH: 1270mm
• Trademark: TIANMA
• Origin: China
• HS Code: 7019310000
• Production Capacity: 2000ton

Product Description

Fiberglass biaxial fabrics

It is a stitch-bonded composite reinforcement combining continuous roving oriented in +/-45 directions into a single fabric.
It can be with mat or without mat .
It is ideal for applications such as wind blades,marine panel ,snowboards,truch and trailer panels...

Products Property:

No any binder ,good compatible with Multi-Resin
Optimal mechanical performance
Easy workability and low cost


Technical Specification:
 

Product No.	Overall Density	+ 45 ° Roving Density	- 45 ° Roving Density	Chop Density	Polyester Yarn Density
	G/M2	G/M2	G/M2	G/M2	G/M2
EBX160	172.0	80	80	/	6
EBX240	233.0	106	106	/	6
EBX300	306.7	150.33	150.33	/	6
EBX400	407.0	200.5	200.5	/	6
EBX450	457.0	225.5	225.5	/	6
EBX600	607.2	300.6	300.6	/	6
EBX800	807.6	400.8	400.8	/	6
EBX1200	1208.6	601.3	601.3	/	6
EBX400/225	632.0	200.5	200.5	225	6
EBX600/225	832.2	300.6	300.6	225	6
EBX800/450	1257.6	400.8	400.8	450	6
EKBXM1208	682.0	200.5	200.5	275	6
EKBXM1308	732.0	225.5	225.5	275	6
EKBXM1708	882.2	300.6	300.6	275	6
EKBXM2408	1082.6	400.8	400.8	275	6

Package & Storage:

The fabrics should be stored away from heat and moisture, and in their original packaging. The best conditions are : temperatures between 15 and 35 , humidity between 35 and 65%. If the product is not stored under these specifications , it is advisable to condition it in  the workshop for at least 24 hours before use, to prevent condensation. The pallets can be stored in 2 levels(1/1).Tianma  recommends that the material be used according to FIFO(first in, first our)method. It is recommended the use of a spacer plae(10mm) between the pallets