Light Weigt Fiberglass Material for Automotive LFT /Lfrt

• Certification: CE, ISO, RoHS
• Technique: Winding Filament Roving
• Yarn Structure: Bulk Yarn
• Surface Treatment: Vinyl Coated
• Fiberglass Type: E-Glass
• Transport Package: Carton/Pallet
• Model NO.: LFRT
• Specification: 48-64roll/plt
• Trademark: TIANMA
• Origin: Changzhou, China
• HS Code: 7019120090
• Production Capacity: 150000ton/Year

Product Description

ECR14-2000/1000-188 Direct Roving ( LFT PROCESS )
 
Characteristics:
188 direct roving is continual fiber for thermoplastics application, coated with a silane-based, which is compatible with a variety of resins.

188 direct roving for LFT is coated with silane-based and compatible with PP, PA, TUP, and PET resins.
·      Excellent strand integrity, high density, and low fuzz
·      Superior dry-use flow-ability and easy control of glass loading
·      Superior wet-use dispersion & easy impregnation
·      Excellent mechanical property & surface quality.
 

Product Code	ECR14-1000-188
Glass Type	ECR
Sizing type	Silicone
Linear density	1000
Diameter	14

 

Product Code	ECR14-2000-188
Glass Type	ECR
Sizing type	Silicone
Linear Density	2000
Diameter	14

Technical Standards	Linear Density (%)	Moisture Content	Binder Content	Breaking Strength
	ISO 1889	ISO3344	ISO1887	ISO3375
	+/- 5%	≤0.10	0.30+/-0.10	≥0.25

Storage: 
The product should be stored in a cool, water-proof area. It is recommended that the room temperature and humidity be always maintained at 15ºC to 35ºC and 35% to 65% respectively. Please keep the product in its original packaging before being used, avoiding moisture absorption.

Package:
Packed by wooden pallets, the average weight is 22kg.

Roll Weight	260mm
Roll inner Diameter	160mm
Outer Diameter	310mm
Weight	22kg

 

Layers	3	4
Rolls per layer	12
Rolls per pallet	36	48
Weight per pallet	792	1056