Vinyl Ester Resin for FRP Rebar, Pultrusion Process, Fiberglass Roving

• Material: Composite Material
• Transport Package: Drum
• Specification: 220KG/DRUM
• Trademark: TIANMA RESIN
• Origin: Changhou, China
• Model NO.: vinyl ester resin
• HS Code: 3907910000
• Production Capacity: 50000ton/Year

Product Description

Product Description

VINYL ESTER RESIN

 

It is one type of bisphenol A epoxy vinyl ester resin with corrosion, heat resistance and lower shrinkage. TM-V211 is workable for winding chemical pipe and storage tank, anticorrosive floor, etc. And it is suitable for pasting winding, pultrusion, spraying, RTM process. 

,Liquid resin technical data:(25ºC):

Item	Unit	Standard	Test Method
Appearance	---	Light yellow liquid	GB/T8237.6.1.1
Viscosity(25ºC)	mPa·s	150~250	GB/T 7193.1
Gel time(25ºC)	min.	5.0~15.0	GB/T 7193.6
Acid value	mgKOH/g	4~10	GB/T 2895
Solid content	%	57~63	GB/T 7193.3
Thermal stability(80ºC)	hr	≥24	GB/T7193.4.5

Remark :82.2ºC GEL TIME : Resin 100g,50% BPO powder 2%
.Resin casting matrix performance (for reference only)

Item	Unit	Test Value	Test Method
		Casting
Tensile strength	MPa	75	GB/T2567-2008
Tensile modulus	MPa	3000	GB/T2567-2008
Elongation	%	5.85	GB/T2567-2008
Flexural strength	MPa	140	GB/T2567-2008
Flexural modulus	MPa	3000	GB/T2567-2008
HDT	ºC	105	GB/T1634-2004
Barcol	--	40	GB/T3854-2005

Remark:casting matrix should follow GB8237-87
        Hardness system:hardener Butanox m50-1.5%, 0.8%Co/oct 1.0%
        Later Hardness system:Room temperature X24hours+60ºC×3hours + 80ºC×2 hours

 
RESIN CAST PHYSICAL PERFORMANCE

TENSILE STRENGTH Mpa	80
TENSILE MODUL Mpa	3500
BENDING STRENGTH Mpa	130
BENDING MODUL Mpa	3500
BREAKING ELONGATION %	2-3
BARCOL HARDNESS	44
OXYGEN INDEX(BETTER IF FIREPROOF ADDITIVE ADDED)	30
HDT ºC	110

 
PACKING:
1.200KG IRON BARREL ZINC PLATED, MAYBE CHANGED ACCORDING TO CUSTOMER'S NEED.
2.THIS PRODUCT IS EASY TO BURN , THE STORAGE LIFE UNDER 25ºC IS THREE MONTHS, HIGHER TEMPERATURE MAY SHORTEN STORAGE LIFE.
  

 