• Dcpd Base DC191 Resin, Unsaturated Polyester Resin
  • Dcpd Base DC191 Resin, Unsaturated Polyester Resin
  • Dcpd Base DC191 Resin, Unsaturated Polyester Resin
  • Dcpd Base DC191 Resin, Unsaturated Polyester Resin
  • Dcpd Base DC191 Resin, Unsaturated Polyester Resin
  • Dcpd Base DC191 Resin, Unsaturated Polyester Resin

Dcpd Base DC191 Resin, Unsaturated Polyester Resin

Shipping Cost:

Estimated freight per unit.

Freight Cost Calculator
Port: Shanghai, China
Production Capacity: 50000ton/Year
Payment Terms: L/C, T/T, D/P, Western Union, Paypal, Money Gram
Transport Package: Drum
Specification: 220KG/DRUM
Trademark: TIANMA RESIN
Origin: Changhou, China

You Might Also Like

Loading...

Basic Info.

Model NO.
DCPD
HS Code
3907910000
  • Product Description
  • Detailed Photos
  • Packaging & Shipping
Dcpd Base DC191 Resin, Unsaturated Polyester Resin
Product Description

TM-DC191 Unsaturated Polyester Resin 

 DCPD TYPE RESIN

1.Brief Introduction:
TM-191D UPR is a kind of ortho Pre-accelerated thixotropic unsaturated polyester resin, add thixotropic imported silica and other additives, with vertical flow not hang, good water resistance, low shrinkage, high mechanical strength, especially suitable for auto parts

2,   Liquid resin technical data(25ºC):
ItemUnitIndexTest standard
Appearance--Clear pale yellow liquidGB/T8237.6.1.1
ViscosityPa.S0.30~0.45GB/T7193.4.1
Gel timemin5.0~12.0GB/T7193.4.6
Acid valuemgKOH/g18.0~26.0GB/T2895
Non-volatile%62.0~68.0GB/T7193.4.3
Remark:  25ºC gel time test: Resin 50g,   Accelerator EC8:1.5g, Curing agent Butanox M-50:1.0g.
 
3,Resin casting matrix performance(for reference)
ItemUnitMeasured valueTest standard
Cast matrixFRP
Tensile strengthMPa50--GB/T 2567-2008
--310GB/T 1447-2005
Elongation at break%2.0--GB/T 2567-2008
Flexural StrengthMPa110--GB/T 2567-2008
--330GB/T 1449-2005
Impact StrengthKJ/m27.8--GB/T 2567-2008
--243GB/T 1448-2005
HDTºC92--GB/T 1634-2004
Barcol Hardness--4561GB/T 3854-2005
Remark:
1) casting matrix should follow GB/T8237-2005. Curing system: accelerator 0.8%Co/oct 1.0 %, curing agent: Butanox M-50 1.5%.
2) Post-curing of casting matrix: room temperature*24 hours+60ºC*3 hours+110ºC*2 hours.
3) Post-curing of FRP: room temperature*24 hours+60ºC*3 hours+110ºC*2 hours.
 
4,Instruction for use
1) High efficiency colorless accelerator shall be avoided in use. Otherwise, it will be easy to cause poor curing of products, which leads to surface stickiness. Special FRP accelerant such as E4 shall be selected to use.
2) When the ambient temperature is high and the gel time of resin is short, do not reduce the dosage of curing agent, gel retardants should be added as needed.
3) When the humidity of construction environment or the temperature is high, it is also easy to cause the surface to become sticky. Wax liquid can be added appropriately.

5,Storage And Transportation
The loading and transportation must follow the rules in chapter 5 of dangerous chemicals regulations .The products should be stored under 25ºC and avoid the sunlight, heat source ,fire source and radiant point. The shelf life in right environment is 3 months.

6,Safety data sheet(SDS)
Before using this product, please read the SDS of this product in detail.

 
Detailed Photos
Dcpd Base DC191 Resin, Unsaturated Polyester Resin
Dcpd Base DC191 Resin, Unsaturated Polyester Resin
 
Packaging & Shipping
Dcpd Base DC191 Resin, Unsaturated Polyester Resin
Dcpd Base DC191 Resin, Unsaturated Polyester Resin

 

Send your message to this supplier

*From:
*To:
avatar Ms. Carol li
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now