TM-191D Unsaturated Polyester Resin
DCPD TYPE RESIN|
Specifications of liquid resin |
|||
|
Item |
Unit |
Value |
Standard |
|
Appearance |
|
Transparent Sticky Thick Liquid |
|
|
Acid Value |
mgKOH/g |
17-20 |
GB2895 |
|
Viscosity(25ºC) |
mPa.S |
1300-1600 |
GB7193 |
|
Gel Time |
min |
9-12 |
GB7193 |
|
Non-Volatile |
% |
70-78 |
GB7193 |
|
80ºCThermal Stability |
h |
≥48 |
GB7193 |
|
Note: Gel Time is25°C; in air bath; 0.5 ml cobalt isocaprylate solution and 0.5 ml MEKP solution were added into50 gresin |
|||
|
Performance Indexes of Resin Casting Substance |
|||
|
Item |
Unit |
Value |
Standard |
|
Barcol hardness ≥ |
Barcol |
40 |
GB3854 |
|
Tensile strength ≥ |
MPa |
50 |
GB2567 |
|
Tensile modulus ≥ |
MPa |
2700 |
GB2567 |
|
Elongation at break ≥ |
% |
2.0 |
GB2567 |
|
Flexural strength ≥ |
MPa |
85 |
GB2567 |
|
Flexural modulus ≥ |
MPa |
3000 |
GB2567 |
|
Impact strength ≥ |
KJ/m2 |
7.5 |
GB2567 |
|
H.D.T ≥ |
ºC |
70 |
GB1634.2 |
|
Note: Environmental Temperature for Experiment: 23±2°C; relative humidity: 50±5% |
|||
| Products | Yearly capacity |
| Fiberglass roving | 20,0000mt |
| Fiberglass fabric and mat | 5,000mt |
| Unsaturated polyester resin | 200,000mt |
| FRP products | 20,000mt |
| Vinyl ester resin | 5,000mt |
| Adhesive | 2,000mt |
| Sheet molding compound | 10,000mt |
| Fiberglass wall covering | 3000,000sqm |
Suppliers with verified business licenses
Audited Supplier 
){kind=link}
){kind=link}