Item Code:188 ( LFT PROCESS )
188 direct roving is continue fiber for thermoplastics application, coated with a silane-based, which is compatible with a variety of resins.
188 direct roving for LFT are coated with a silane-based and compatible with PP, PA, TUP and PET resins.
· Excellent strand integrity ,high density and low fuzz
· Superior dry-use flow-ability and easy control of glass loading
· Superior wet-use dispersion & easy impregnation
· Excellent mechanical property & surface quality.
Product Code |
ECR14-1000-188 |
Glass Type |
ECR |
Sizing type |
Silance |
Linear density |
1000 |
Diameter |
14 |
Product Code |
ECR14-2000-188 |
Glass Type |
ECR |
Sizing type |
Silance |
Linear Density |
2000 |
Diameter |
14 |
Technical Standards |
Linear Density (%) |
Moisture Content |
Binder Content |
Breaking Strength |
ISO 1889 |
ISO3344 |
ISO1887 |
ISO3375 |
+/- 5% |
≤0.10 |
0.30+/-0.10 |
≥0.25 |
Storage:
The product should be stored in a cool, water-proof area. It is recommended that the room temperature and humidity be always maintained at 15ºC to 35ºC and 35% to 65% respectively. Please keep the product in its original packaging before being used, avoiding moisture absorption.
Roll Weight |
260mm |
Roll inner Diameter |
160mm |
Outer Diameter |
310mm |
Weight |
22kg |
Layers |
3 |
4 |
Rolls |
12 |
Rolls/Layer |
36 |
48 |
Weight/Pallet |
792 |
1056 |
Package:
The product can be packed in bulk bags and composite plastic woven bags.
Bulk bags can hold 900kg-1000kg each.
Composite plastic woven bags can hold 15kg-25kg each.
Combotex Roving (PP+FIBERGLASS)
Combotex roving
(PP+FIBERGLASS
)is a kind of high performance prepreg which is made of glass fiber coated with PP resin ,which can be directly used to form PP resin composite, without additional resin .
The applicable forming process of this product includes molding, vacuum forming, pultrusion and winding forming. Its application fields cover aerospace, automotive industry, construction, sports equipment, new energy, etc.
Product Code |
Type of fiber |
Resin |
Fiberglass content |
Linear density (tex) |
Product color
|
CH-PP60/1870N |
E/ECR-GLASS |
Polypropylene resin |
60% |
1870 |
Natural or Black |