https://tianmagroup.en.made-in-china.com/product/LSyEjmTUaCYr/China-Glass-Fiber-Woven-Roving-Ewr800-100.html
Product Description
TM-2250 is an unsaturated polyester resin specially designed for polyester concrete. It has low viscosity, low shrinkage, good wettability with fillers to maintain high filler filling rate, less styrene volatilization, improved working environment, and good air-drying. It can prevent the surface of the molded product from sticking in a short time. Suitable for making large products.
Item |
Unit |
Standard Data |
Test Method |
Appearance |
|
Light yellow liquid |
GB/T8237.6.11 |
Viscosity |
Pa.s |
0.13-0.17 |
RS-V004 |
Gel Time |
Min. |
9.0-13.0 |
GB/T7193.4.6 |
Acid Value |
mgKOH/g |
9.0-17.0 |
GB/T2895 |
Solid Content |
% |
66.0-72.0 |
GB/T7193.4.3 |
VINYL ESTER RESIN
MODEL:TM-V211
(HIGH FLEXIBILITY CORROSION RESISTANCE EPOXY VINYL ESTER RESIN)
LIQUID RESIN CHEMICAL PERFORMANCE
COLOR |
LIGHT YELLOW TRANSPARENT LIQUID |
VISCOSITY mPa.s(25ºC) |
250-450 |
GEL TIME min (25ºC) |
5-30 |
HEAT STABILITY(80ºC) |
>24 |
RESIN CAST PHYSICAL PERFORMANCE
TENSILE STRENGTH Mpa |
80 |
TENSILE MODUL Mpa |
3500 |
BENDING STRENGTH Mpa |
130 |
BENDING MODUL Mpa |
3500 |
BREAKING ELONGATION % |
2-3 |
BARCOL HARDNESS |
44 |
OXYGEN INDEX(BETTER IF FIREPROOF ADDITIVE ADDED) |
30 |
HDT ºC |
110 |
PACKING:
1.200KG IRON BARREL ZINC PLATED, MAYBE CHANGED ACCORDING TO CUSTOMER'S NEED.
2.THIS PRODUCT IS EASY TO BURN , THE STORAGE LIFE UNDER 25ºC IS THREE MONTHS, HIGHER TEMPERATURE MAY SHORTEN STORAGE LIFE.